Normal
Steel
|
International code AISI
|
Europe code DIN
|
Steel brand
|
Factory hardness
|
Anti-stress strength
|
Heat treatment method
|
Categories and
applications
|
1045 1040 1050
|
1.1730
|
ASSAB 760 K-100 DAIDO
P1
|
13~18HRC
|
600N/m㎡
|
Water quenching
|
King brand, usually for die holder plate, ejecting pin
plate, support head and curb pin
|
P20
|
1.2738
|
ASSAB 718 DAIDO
P88X,P-5 DESHENG 2311 A FINKL P20
|
28~32HRC
|
915N/m㎡~
1100N/m㎡
|
Usually for inner die
inlay parts
|
No hardness but common
plastic inner die is needed.
|
P20H
|
1.02711
|
ASSAB 718 HI DESHENG
711 A FINKL P20H
|
35~38HRC
|
1000N/m㎡~
1200N/m㎡
|
No hardness
|
common plastic inner
die is needed.
|
H-13
|
1.2344
|
ASSAB 8407 A FINKL H13
DESHENG 2344 ESR
|
190 HB
(12HRC)
|
650N/m㎡
(hardness to1400N/m㎡)
|
Fine inlay piece wind
quench large inlay piece oil quench double tempering
|
Do not be used for die,
ejecting, skate board, and ejecting pin, hardness to 48~52HRC
|
0-1
|
1.2510
|
ASSAB DF-2 DESHENG
25100
|
180H-220 HB (10~18HRC)
|
|
Oil quench
|
For low temperature
working skate gasket, inlay and strip hardness to 54~56HRC
|
S-7
|
|
ASSAB S-7 DESHENG 2379
|
200HB
(15HRC)
|
|
At least three times
tempering for oil quench
|
Usually for shock die,
press board and gasket hardness to 54~56HRC
|
420
|
1.2083
|
STAVAX S-136 A FINKL
420 DESHENG 2083 ESR
|
180~200HB
(10~15HRC)
|
High temperature
tempering
915~
1200N/m㎡
|
Double tempering for
oil and win tempering
|
common application:48~52hrc
mirror polishing piece is needed:52~54HRC
injection PVC piece:46~48HRC
|
420H
|
1.2316
|
S-136H DESHENG 2316 ESR
|
32~34HRC
|
915~1200N/m㎡
|
No hardness is needed
|
It fits for injection
pvc with good corrosion resistant property.
|
P4
|
1.2341
|
ASSAB 8416
|
95~100HB
|
|
Surface carburization
|
Cladding steel: for
complex mode steel, duplicate money and button (rarely use at
present)hardness to 62HRC
|
D2
|
1.2379
|
ASSAB XW41
|
210~240HB
(15~22HRC)
|
|
tempering for oil quench
|
Cooling steel: for die,
pin, inlay, wear proof piece and plastic material diving inlay
|
BeCu
|
|
MOLDMAX DESHENG B2
|
40~42HRC
|
1240N/m㎡
|
Age hardening (330℃/3hr)
|
Beryllium copper:
Featured by fast heat transmission, it’s useful to go where the water can not
reach.
|
A1-Bronze
|
|
Cup copper
|
|
|
|
It is harder than
bronze and fits for inner mold cavity inter-lock, which can reduce working
loss.
|